Influence of Аl and Mn impurities on structural processes transformations in copper alloys

Authors

  • V. A. Lobodyuk G. V. Kurdyumov Institute for Metal Physics of the N.A.S. of Ukraine, 36, Academician Vernadsky Boulevard, UA-03142 Kyiv, Ukraine
  • K. M. Mukashev Faculty of Physics and Technology, al-Farabi Kazakh National University, 71, al-Farabi Ave, 050040, Almaty, Republic of Kazakhstan http://orcid.org/0000-0002-3568-7143
  • D. E. Tolen Faculty of Physics and Technology, al-Farabi Kazakh National University, 71, al-Farabi Ave, 050040, Almaty, Republic of Kazakhstan

DOI:

https://doi.org/10.26577/phst.2020.v7.i2.04
        40 40

Abstract

In the work on specific examples involving real copper-based alloys containing 14 weight %Al and 3 weight
%Mn, describes the results of a study of the process of restoring the shape of a material that was defomated
according to the three-point bending scheme. The studies were carried out by measuring changes in the
temperature dependence of the electrical resistance and deflection of the sample, as well as by obtaining
microelectronograms using an electron microscope. It is established that martensitic crystals that occur in
hardened samples have a high density of packing defects and thin twins formed on the (121) γ´ plane.

Downloads

How to Cite

Lobodyuk, V. A., Mukashev, K. M., & Tolen, D. E. (2020). Influence of Аl and Mn impurities on structural processes transformations in copper alloys. Physical Sciences and Technology, 7(3-4), 26–31. https://doi.org/10.26577/phst.2020.v7.i2.04

Issue

Vol. 7 No. 3-4 (2020): PHYSICAL SCIENCES AND TECHNOLOGY

Section

Condensed Matter Physics and Related Techology

License

Contributor hereby grants to the "Physical Sciences and Technology" the full and exclusive rights to reproduce, publish, republish, prepare all foreign language translations and other derivative works of an article in any kind of electronic media and print editions.