Study of structural changes in ZrO2 ceramics irradiated with heavy ions of Kr15+ with an energy of 147 MeV.

Abstract

This paper presents the results of a study of changes in structural characteristics, such as the degree of
crystallinity, dislocation density, and deformation of the crystal lattice in ZrO2 ceramics as a result of
irradiation with heavy Kr15+ ions with an energy of 147 MeV. The choice of the type of irradiation ions
is due to the possibility of simulating the processes of defect formation comparable to the irradiation of
radiation-resistant materials by fragments of uranium fission. The radiation doses ranged from 5х1013 to
1х1016 ion/cm2. The dependences of the change in the crystallographic parameters on the radiation dose
were established. At the same time, the maximum decrease for an irradiation dose of 1x1016 ion/cm2 was no
more than 10 %, which in turn indicates a high radiation resistance to the accumulation of defects during
large-dose irradiation. It was determined that the greatest change in the degree of crystallinity is observed
above a dose of 1х1015 ion/cm2. The data obtained indicate a high degree of resistance of these ceramics to
radiation damage.